The Zn2Te3O8-30%TiTe3O8(ZTT) powder was prepared using the solid state reaction technique, and sintered at temperature low than 600 ℃ in atmosphere furnace. Then the samples were analyzed by XRD, SEM and microwave network analyzer. The result showed that ZTT could be sintered in ultra low temperature with pretty good dielectric properties(at 1 MHz measured frequency, the dielectric constant and the dielectric loss were 19～27 and low than 3%, respectively,at high frequency,the Q×f and τf of ZTT ceramics were 56 191 GHz and 1.66 μ℃-1, respectively).Thus it was possible to produce low cost thin film capacitance.